A New Role of Ml Type Dopant for Nd-Rich Nd-Fe-Co-B Nanocrystalline Ribbons
In this work, our attempts focused on Ge effects on magnetic-microstractural relationships in Nd-Fe-Co-B nanocrystalline ribbons. Based on Transmission Electron Microscopy (TEM) and three dimensional atom probe (3DAP) analysis, it was observed that Ge containing alloys have a new behavior that was not observed yet. The increase of Ge content up to 0.36at％ caused the increase of Br and (BH/)max due to increase of Co content of Nd2Fe14B phase. However, the magnetic properties deteriorated for Ge bearing samples beyond 0.36at％ due to the decrease of volume fraction of Nd2Fe14B phase. The comparison of Ge and Ga (another Ml dopant) effects on coercivity was reported and microstructural studies (using TEM and 3DAP) were shown the Nd-rich phase morphology and its alloying elements distribution in the nanometer sized intergranular phase.
Nd-Fe-Co-B nanocrystalline ribbon M1 dopant
Reza Gholamipour Ali Beitollahi Vahak Marghusian Tadakatsu Ohkubo Kazuhiro Hono
Iran Research Organization for Science and Technology (IROST) Iran University of Science and Technology (IUST) Japan National Institute for Materials Science (NIMS)
国际会议
北京
英文
215-220
2006-08-29（万方平台首次上网日期，不代表论文的发表时间）