Practice on a High Carbon High Strength Steel Produced by Compact Strip Production

CSP is proved to be an effective way to produce high carbon high strength steel strip with reduced cost and good quality. A kind of high carbon high strength low alloy steel strip was developed at Lianyuan Steel. The steel 65Mn with the carbon content of 0.65% had yield strength 490MPa, tensile strength 870MPa and elongation 18%. The strength of 65Mn produced by CSP was appromximately 40% larger than that produced by traditional process. Observations of electron microscopy revealed that the microstructures of the strip consisted of fine-grained ferrite and pearlite. Nano sized pearlite lamellar spacing was observed in the steel strip. Compared with the conventional process, the grain size of the steel strip produced by CSP was much smaller. Fine and dispersed precipitations were also observed in the as-rolled specimens.

CSP high carbon high strength low alloy steel ferrite pearlite

JIAO Guo-hua ZHOU Chun-quan ZHANG Liang-zhou Wen De-zhi ZHOU Ming-wei HUANG Gang WU Kai-ming

Hunan Valin Lianyuan Iron and Steel Co.Ltd, Loudi 417009, Hunan, China Department of Applied Physics,Wuhan University of Science and Technology, Wuhan 430081, Hubei, China

国际会议

2009年薄板坯连铸连轧国际研讨会(TSCR 2009)(2009 International Symposium on Thin Slab Casting and Rolling)

南京

英文

372-376

2009-05-13(万方平台首次上网日期,不代表论文的发表时间)