Fabrication and Characteristics of Yb3+-doped silica optical fibers

摘要：

A kind of single cladding highly Yb3+-doped silica optical fiber was fabricated by a new furnace round heating MCVD process. The best temperature of deposition pass and that of sensitive presintering pass were presented, the absorption of it achieved 594dB/m at 976nm and its background loss was only 0.1dB/m.