Synthesis and electrical properties of Co-doped Y0.08Sr0.92TiO3-δ as a potential SOFC anode
Strontium titanate with perovskite structure is one of potential candidates for alternative anodes for solid oxide fuel cells. Co-doped Y0.08Sr0.92TiO3-δwas synthesized via solid-state reaction. The effect of Co-doping on the electrical behavior of Y0.08Sr0.92TiO3-δ was investigated and a doping mechanism was proposed. Compared with Y0.08Sr0.92TiO3-δ, the electrical conductivities of Y0.08Sr0.92CoxTi1-xO3-δ decrease obviously with increasing Co-doping amount at 25-1000℃, while the ionic conductivities increase significantly at 500-1000℃. The addition of Co can increase the oxygen vacancy concentration and enlarge the saddle point critical radius rc both of them should be responsible for the remarkably enhanced ionic conductivity of Y0.08Sr0.92CoxTi1-xO3-δ. The decreased electronic conductivity of Y0.08Sr0.92CoxTi1-xO3-δ is ascribed to the lowered Ti3+concentration, caused by the substitution of Co3+. Co-doping increases the oxygen absorption temperature, and thus widens the operation temperature range of doped-SrTiO3.
Co-doped Y0.08Sr0.92TiO3-δ Anode Ionic conductivity Mized conductor Solid ozide fuel cell
Xue Li Hailei Zhao Feng Gao Zhiming Zhu Ning Chen Wei Shen
Department of Inorganic Nonmetal Materials, University of Science and Technology Beijing, China, Bei Department of Inorganic Nonmetal Materials, University of Science and Technology Beijing, China, Bei Department of Mechanical Engineering, Tsinghua University, Beijing 100084, PR China
国际会议
The 16th International Conference on Solid State Ionics(第十六届国际固态离子学会议)
上海
英文
1588-1592
2007-07-01（万方平台首次上网日期，不代表论文的发表时间）