Rate capability of lithium intercalation into nano-porous graphitized carbons

Nano-porous graphitized carbons were successfully prepared by using mono-dispersed SiO2 colloidal crystal as a template and mesophase pitch as a carbon source with final heat treatment temperatures (IITT) of 1000-2500℃. Rate capability of lithium intercalation/de-intercalation of the nano-porous graphitized carbons was investigated. 35-60% of capacities were retained when the current density was increased from 37.2 mA g-1 to 372 mA g-1. Electrochemical impedance spectra indicated that formation of SEI layers caused increased polarization.

Lithium ion battery Porous carbon Graphite

Hirotoshi Yamada Yuko Watanabe Isamu Moriguchi Tetsuichi Kudo

Faculty of Engineering, Nagasaki University, 1-14, Bunkyo-machi, Nagasaki 852-8521, Japan Graduate School of Science and Technology, Nagasaki University, 1-14, Bunkyo-machi, Nagasaki 852-852 National Institute of Advanced Industrial Science and Technology, Tsukuba Central 2, 1-1-1, Umezono,

国际会议

The 16th International Conference on Solid State Ionics(第十六届国际固态离子学会议)

上海

英文

1706-1709

2007-07-01(万方平台首次上网日期,不代表论文的发表时间)