The Effects of Additives on Yields and Distribution of Gasand Liquid from Pyrolysis of Biomass by Microwave Heating
Pyrolysis of pine wood sawdust was carried out by microwave heating at ca.470℃ under dynamic nitrogen atmosphere. Eight inorganic additives(NaOH,Na2CO3,Na2SiO3,NaCl,TiO2.HZSM-5,H3PO4.Fe2(SO4)3)were investigated in terms of their catalytic eriects on the pyrolysis.All of the eight additives have increased yields of solid products greatly and decreased yields of gaseous products more or less.Yields of liquid products have not subjected to dramatic change.The incondensable gases produced from pyrolysis consist mainly of H2,CH4,CO and CO2.All of the eight additives have made these gases evolve earlier,among which the four sodium additives have the most marked effect.All the additives have made the amount of CH4 and CO2 decrease,while all of them except NaCl,TiO2 and Fe,(SO4)3 have made that of H2 increase and all of them except Na2SiO3 and HZSM-5 have made that of CO decrease.Alkaline sodium compounds NaOH, Na2CO3 and Na2SiO3 favor H2 formation most.The most abundant organic component in the liquid products from pyrolysis of untreated sample and samples treated by all the additives except H3PO4 and Fe2(SO4)3 is acetol.All the four sodium compounds favor acetol formation reaction and the selection increasing effect follows the order of NaOH> Na2CO3≈Na2SiO3>NaCl.TiO2 goes against the formation of acetol,HZSM-5 has no marked effect on acetol formation. The two dominant organic components identified in the liquid products from pyrolysis of H3PO4 and Fe2(SO4)3 treated samples are both fufural and 4-methyl-2-methoxy-phenol.Organic composition of liquid products from the microwave pyrolysis of sawdust in this study is quite different from that by conventional heating and the underlying causes forming this difference is tentatively proposed.
pyrolysis pine wood biomass microwave additives
CHEN Mingqiang WANG Jun CHEN Minggong WANG Fengchan MIN Fanfei ZHANG Mningxu
School of Chemical Engineering,Anhui University of Science and Technology,Huainan 232001,China School of Material Engineering,Anhui University of Science and Technology,Huainan 232001,China
国际会议
合肥
英文
513-516
2008-06-05（万方平台首次上网日期，不代表论文的发表时间）