PerformanceTest Of Ps/Fly Ash Slurry Grouting Into Soil Fracture At The Ruins Of Jiao He
After the PS-(F+R) slurry is prepared by mixing PS as binding ingredient,fly ash generated from thermal power plant and powdered adobe at the Ruins of Jiaohe as filling substance and sodium fluosilicate as curing agent,its initial setting time is got and its shrinkage behaviour is monitored.The mechanical strength of PS-(F+R) grouting material is tested at different age and the effect of factors,such as curing temperature,amount of sodium fluosilicate,modulus of PS,concentration of PS and water-ash ratio to strength is also discussed.Furthermore,durability experiment including its resistance to water,to disintegration induced by freezing and thawing,to crystallization and to aqueous alkali is carried out.It is showed that the curing process of PS-(F+R) grouts is moderate and can be adjusted,the linear shinkage is around 2.5% under the PS to filler ratio in mass of 0.60,the long term strength is overwhelmingly determined by PS concentration,and the performance of durability is pretty good.
Fracture grouting PS-(F+R) grouts PS fly ash silt adobe curing agent
YANG Tao LI Zuixiong WANG Wanfu
College of Culture and Museology,Northwest University,Xian 710069 China Conservation Institute,Dunhuang Academy,Dunhuang,Gansu 736200,China Technical and Service Center for Protection of Cultural Relics.Dunhuang Academy,Dunhuang
国际会议
甘肃敦煌
英文
320-324
2008-09-22（万方平台首次上网日期，不代表论文的发表时间）