Development of a Process Flow Sheet for Nickel Recovery from Chromite Concentration Plant Tailings
Recovery of nickel and chromite from the tailings has been studied on the samples with 0.214 %Ni and 5. 10 % Cr2O3 content and taken from Orhaneli Chromite Concentration Plant. Mineralogical examinations of the samples showed the existence of chromite, olivine, pyroxene, chrysotile, antigorite, chlorite, idingite, tremolite and calcite together with trace amounts of millerite, pentlandite,pyrite, pyrrhotite, hematite and iimonite type iron oxide minerals in partially serpantinized dunite type particles.In order to recover chromite from Chromite Concentration Plant tailings Mozley Table and Knelson Separator are used and concentrates containing approximately 42% and 46% Cr2O3 are produced respectively with 40% recovery. Most of the nickel remained in the tailings. Therefore,acidic leaching tests are performed in order to dissolve nickel from these tailings. Effects of particle size, acid concentration, temperature, leaching time and solid/liquid ratio on the nickel leaching efficiency are investigated. The optimum leaching conditions are found as 250 g/L acid concentration,1/5 solid/liquid ratio, 2 hours of leaching time and 60℃ temperature, almost all nickel is dissolved at the optimum conditions and acid consumption is about 841 kg/t.Repeated leaching tests are carried out in order to have enough Ni content in the leach liquor for the further treatment of solutions. After repeated leaching tests, leach liquor contains 3 kg/m3 Ni, 48kg/m3 Fe, 2.2 kg/m3 Si, 23 g/m3 Cr and 590 kg/m3 H2SO4. Ni is recovered from that solution by precipitating with H2S followed by HNO3 dissolution and precipitating Ni as hydroxide with 63% Ni content.Leach cakes are subjected to the gravity separation (Mozley table) to recover the remained chromite and a chromite concentrate with 47% Cr2O3 content is produced with 53% recovery.As a result of the abovementioned tests, a conceptual process flow sheet is proposed for the treatment of these chromite concentration plant tailings.
Acid leaching Nickel Chromite Gravity Concentration Tailings
G. (O)nal F. Arslan N. Acarkan A. E. Acma A. Gül A. S. (Alpyildiz) F. Burat V. Gürkan
Mineral Processing Engineering Dept. Mining Faculty Istanbul Technical University, Istanbul, Turkey
国际会议
XXIV International Mineral Processing Congress(第24届国际矿物加工大会)
北京
英文
2570-2575
2008-09-24（万方平台首次上网日期，不代表论文的发表时间）