Effect of post-synthesis hydrothermal treatment on pore size expansion of silica mesoporous molecular zeolite

The cheaper industrial inorganic silicate Na2O·3.3SiO2 was selected as silica source, using CH3(CH2)15·(CH3)3NBr surfactant as template, adding the organic amine by post-synthesis hydrothermal treatment, and the supported vanadium mesoporous materials was prepared by hydrothermal synthesis. The results indicated the pore size expansion of silica mesoporous molecular zeolite was different according with the different organic amine and post-hydrothermal temperature in the mesoporous materials synthesis. It was shown that the use of DMDA and TEA to restructure MCM-41 with 3.94 nm pores prepared under conventional hydrothermal synthesis afforded mesoporous silica with up to 6.62 and 9.30 nm pores, respectively. 2.36 times expansion of pore size for TEA and 68% improvement for DMDA was achieved successfully.

Mesoporous Molecular Sieve V-MCM-41 Tunable pore size

许俊强 储伟 郭芳

重庆工学院生物工程学院,重庆 400050 四川大学化学工程学院,成都 610065

国际会议

第六届中国国际纳米科技研讨会

成都

英文

2007-11-19(万方平台首次上网日期,不代表论文的发表时间)