(0) A novel composite was prepared from dough-modeling compound (DMC) reinforcement and Ethylene propylene diene terpolymer (EPDM) / acrylic rubber (ACM) matrix. DMC/EPDM/ACM mass ratio and vulcanizing process were studied by testing tensile strength, Shore A hardness, elongation at break, wear and thermal properties. The results showed that the mechanical properties, thermal properties and wear resistance of the composites were good when DMC/EPDM/ACM mass ratio was 70/25/75, and the cure condition was at 180°C under 10 MPa for 25 min. The cross linking structure of the composites was studied by IR, which further proved the interaction between DMC, ACM and EPDM.