Electro-magnetism of peg-20000 doped with nano-cobalt ferrite oxide powder containing La3+
The sol-gel method was used to prepare three kinds of nanometer magnetic particles,such as the nano-cobalt ferrite oxide powders and those doped by LaCl3·nH2O.In the thermo-decomposition process of the precursors to get these magnetic particles,TG/DTG was applied to investigate their character.The prepared magnetic particles with average diameter less than 100 nm were characterized by XRD and TEM.The results show the difference between the activation energies of these particles in different thermo-decomposition stages,even not in the same stage for different samples.The cobalt ferrite doped with La3+ affects its saturation magnetization(ms) and coercive force(Hc).As CoCl2·6H2O is partly substituted by La3+,the value of Hc decrease with the increase of ms.When FeCl2·4H2O is partly substituted by La3+,Hc increases obviously.The three kinds of nanometer magnetic particles were doped into polyethylene glycol-20000 (peg-20000) with different ratios respectively to obtain compound substance with optimal conductivity of 0.686 S/m.
nanometer particle thermo-decomposition process magnetism conductivity polymer films
XIAO Li FANG Zheng QIU Guan-zhou LIU Jian-she
Hunan Metallurgic Professional Technical College,Zhuzhou 412000,China;School of Chemistry and Chemic School of Chemistry and Chemical engineering,Central South University,Changsha 410083,China School of Resources Processing and Bioengineering,Central South University,Changsha 410083,China
国际会议
2007年国际有色金属大会(International Conference of Nonfereous Materials 2007)(ICNFM)
长沙
英文
2007-11-28（万方平台首次上网日期，不代表论文的发表时间）