Full Color and Monochrome PM PLED FPDs Made with Solution Processes
1.5 inch diagonal red, green, and blue monochrome passive-matrix (PM) polymer light emitting diodes (PLED) flat panel displays (FPDs) with format 96 × 64 were fabricated by spin-coating technology with device structure of ITO/PEDOT/Emissive layer/Ba/Al. By rearranging the location and the direction of the panel with respect to the center of the spinner, the piling of organic materials under the cathode separator was significantly reduced, resulting in a more uniform light emission. The final display showed neither dead pixels nor dead lines. Current efficiencies of 1. 37, 9. 5 and 1.44 cd/A, and CIE color coordinates of (0.62, 0.37), (0.37, 0.60) and (0.15, 0.13), for red, green, and blue monochrome displays, respectively, have been achieved. Further, 1.5 full color PM PLED FPDs with format 96 × RGB × 64 was successfully fabricated by inkjet printing technology. The current efficiency was more than 1 cd/A at full screen white with color coordinates located at (0.34, 0.35). A color gamut of 50％ NTSC was obtained. For all the displays, the 5-point uniformity was more than 80％.
Junbiao Peng Qiaoli Niu Yuxuan Shao Wei Xu Lei Wang Shaohu Han Nanliu Liu Yong Cao Jian Wang
Institute of Polymer Optoelectronic Materials and Devices,South China University of Technology, and Key Lab of Specially Functional Materials, Ministry of Education, Guangzhou 510640, China
国际会议
上海
英文
387-391
2007-03-12（万方平台首次上网日期，不代表论文的发表时间）