Synthesis of Yttrium Aluminum Garnet (YAG: Ce ) Phosphor by Co-precipitation Method

摘要：

YAGCe precursor was prepared by a co-precipitation method from a mixed solution with aluminum, cerium and yttrium ions, and Y3Al5O12: Ce3+ phosphor was successfully synthesized after baking the as-prepared precursors up to 1 100℃ and reducing by N2/H2 atmosphere at 1 400℃. The XRD and SEM analysis indicate that the YAG:Ce phosphor powders have better particle shape and smaller particle size than phosphor prepared by high temperature solid state reaction method. The luminescence spectrum analysis show that, the YAG:Ce phosphor shows a strong fluorescence emission when excited by 465 nm blue light.

关键词： YAGCe Phosphor Co-precipitation Luminescence Spectrum

作者: Zhisen Wu Tong Cao Jing Wu Yan Dong Jianqing Jiang Chao Zhang

作者单位: School of Materials Science and Engineering, Southeast University,Nanjing 211189, China Jiangsu Subote new material Co.. Ltd. Nanjing 210008, China

会议类型: 国际会议

会议名称: 2007亚洲显示国际会议（AD07）

会议地点: 上海

会议语种:英文

页码: 1853-1856

在线出版日期: 2007-03-12（万方平台首次上网日期，不代表论文的发表时间）