Manufacture Technology and Nondestructive Test of Wood / Waste Styrofoam Composite

摘要：

Manufacture technology of wood / waste styrofoam composite was investigated. The possibility that the dynamic Youngs modulus of wood / waste styrofoam composite can be measured by nondestructive testing method was also discussed. The following conclusions have been drawn. Wood / waste styrofoam composite can be manufactured under the hot press condition of 155℃, 1 MPa for 7 minutes. The dynamic Youngs moduli measured by longitudinal transmission method were bigger than those measured by longitudinal vibration method and flexural vibration test. The dynamic Youngs moduli measured by in-plane flexural vibration test were less than those measured by out-plane flexural vibration test.

关键词： wood / waste styrofoam composite manufacture technology nondestructive test dynamic youngs modulus

作者: HU Ying-cheng

作者单位: Key Laboratory of Bio-based Material Science and Technology of Ministry of Education, College of Material Science and Engineering,Northeast Forestry University, Harbin 150040, China

会议类型: 国际会议

会议名称: 2006中日稻米品质测控及美味技术学术研讨会

会议地点: 北京

会议语种:英文

页码: 229-230

在线出版日期: 2006-08-03（万方平台首次上网日期，不代表论文的发表时间）