Effects Of Residual Stress On Corrosion Behavior Of X80 Pipe Base Metal
The influence of residual stress on stress corrosion behavior was studied by way of SSRT test on the base metal of X80 pipe with different residual tensile stress in the simulating soil environment aqueous solution; and the electrochemical test techniques were adopted to test the effect of the residual stress on electrochemical polarization behavior and AC impedance characteristics of the base metal.It is shown that the base metal specimens without introducing the residual stress of X80 UOE pipe and X80 SAWH pipe have different stress corrosion sensitivity in this solution.The base metal specimens with different residual stress of X80 pipe only occurs the anodic metal dissolution reaction on the material surface in this kind of solution without forming the passive film.The residual tensile stress leads to the increase of the electrochemical activity and the reduction of impedance of the base metal surface of X80 pipe,and it accelerates the nucleation and early propagation of the stress corrosion crack,which promotes the SCC sensitivity of the base metal.
X80 pipe residual stress corrosion
XIONG Qingren LUO Jinheng HU Meijuan ZHANG Weiwei ZHANG Liang
Tubular Goods Research Institute of CNPC Key Laboratory of Petroleum Tubular Goods Engineering of CNPC Xi”an,China
国内会议
西安
英文
1-5
2015-04-27（万方平台首次上网日期，不代表论文的发表时间）