Effect of heat-affected zone(HAZ)on spot weldability in automotive hot stamping(HS)steel sheet was investigated for automotive applications.Tensile test was performed on a tensile testing machine at a crosshead speed of 3 mm/min,using spot welded test specimen(Parallel length: 60 mm,Width: 20 mm,Thickness: 1.4 mm,Tab: 20×20 mm).The spot welding test was carried out using spot welded test specimen with welding current(I)of 6.3 kA to 9.5 kA.Hardness was measured with the dynamic ultra micro Vickers hardness tester.In HS steel,has very high strength of 1 500 MPa,tensile strength(TS)and total elongation(TEl)of the spot welded test specimen of HS steel were lower than those of base metal test specimen.The spot welded test specimen broke in the weld.The Vickers hardnesses(HVs)of base metal and fusion zone of hot stamping steel were around HV500.In addition,the hardness of HAZ was under HV300.The difference of hardness between fusion zone and HAZ was around HV200.The hardness distribution acted as a notch.On the other hand,in dual phase(DP)steel,has low strength of 590 MPa,the TS of spot welded test specimen of DP steel was the same as the base metal test specimen because of the breaking of base metal.The TEl of the spot welded test specimen of DP steel was smaller than that of base metal test specimen.In the spot welded test specimen of DP steel,the hardness of base metal was around HV200 and the fusion zone was around HV500.The hardness distribution did not act as a notch.The difference in hardness between base metal and HAZ acted on a crack initiation at HAZ softening.
Department of Mechanical Engineering,National Institute of Technology,Nagano College,716 Tokuma,Naga Kobe Steel,Ltd.,Technical Development Group,1-5-5 Takatsukadai,Nishi-ku,Kobe,Hyogo 651-2271 Japan Department of Mechanical Engineering,Faculty of Engineering,Iwate University,4-3-5 Ueda,Morioka,Iwat Department of Electrical and Control Engineering,National Institute of Technology,Nagano College,716 Advanced Courses,National Institute of Technology,Nagano College,716 Tokuma,Nagano 381-8550 Japan.