DEVELOPMENT AND TECHNOLOGY OF LARGE THICKNESS TMCP STEEL PLATE WITH 390MPA GRADE USED FOR ENGINEERING MACHINERY
Recently,with the rapid upgrading of the equipment in the steel Corp,the rolling technology of TMCP has been rapidly developed and widely applied.A large amount of steel plate has been produced by using the TMCP technology.The TMCP processes have been used more and more widely and replaced the heat treatment technology of normalizing,quenching and tempering heat process.In this paper,low financial input is considered in steel plate production and the composition of the steel has been designed with low C component,a limited alloy element of the Nb,and certain amounts of Mn element.During the continuous casting process,the size of the continuous casting slab section is 300 mm × 2400 mm.The rolling technology of TMCP is controlled at a lower rolling and red temperature to control the transformation of the microstructure.Four different rolling treatments are chosen to test its effects on the 390MPa grade low carbon steel of bainitic microstructure and properties.This test manages to produce a proper steel plate fulfilling the standard mechanical properties.Specifically,low carbon bainite is observed in the microstructure of the steel plate and the maximum thickness of steel plate under this TMCP technology is up to 80mm.The mechanical property of the steel plate is excellent and the KV2 at-40℃ performs more than 200 J.Moreover,the production costs are greatly reduced when the steel plate is produced by this TMCP technology when replacing the current production process of quenching and tempering.The low cost steel plate could well meet the requirements of producing engineering machinery in the steel market.
Low carbon bainitic TMCP 390MPa grade Large thickness
Xiaoshu WANG Zhijun ZHANG Peng ZHANG
Wuyang Iron and Steel Co.,Ltd Wugang,Henan,462500,China
国内会议
杭州
英文
961-966
2015-11-11（万方平台首次上网日期，不代表论文的发表时间）