Solvothermal In-situ Sythesis of Superhydrophobic ZnS Film
In this work,a superhydrophobic ZnS film was successfully synthesized by a simple solvothermal route using Zn foil and sulphur powder as raw materials in an absolute ethanol solution at 160 ℃for 24 h.The products were characterized by X-ray diffraction (XRD),energy dispersive spectroscopy (EDS),scanning electron microscopy (SEM),and contact angle (CA).Results show that the obtained films were high crystallinity and uniformity.A possible reaction mechanism was proposed and discussed.It is found that the ZnS film exhibits superhydrophobicity due to its special nanoflakes structure.The average thickness of the ZnS nanoflakes film is ~120 nm.ntroduction
Zinc sulphide nanoflakes superhydrophobicity
Yidong Zhang Pinjiang Li
Key Laboratory for Micro-Nano Energy Storage and Conversion Materials of Henan Province, Institute of Surface Micro and Nano Materials, Xuchang University, Xuchang, Henan Province, 461000, P.R. China