摘要：

The response and failure of brass H62 specimens subjected to different levels of pre-loaded stresses and heating rates were investigated using a Gleeble-1500 thermal-mechanical material testing system. The metallographs of the tested material were also observed and analyzed. It is found that the increase of either pre-loaded stress or heating-rate decreases the failure temperature. Metallographic analysis shows that high heating-rate may cause stronger local thermal inconsistency (LTI) and remarkably increase the microdefects in the material, which may markedly degrade the macroscopic mechanical properties of the material.

关键词： brass H62 pre-loaded stress heating rate failure temperature local thermal inconsistency

作者: CHEN Bin PENG Xiang-he FAN Jing-hong SUN Shi-tao

作者单位: College of Resource and Environment Science,Chongqing University,Chongqing 400044,China

会议类型: 国际会议

会议名称: 2007年国际有色金属大会(International Conference of Nonfereous Materials 2007)(ICNFM)

会议地点: 长沙

会议语种:英文

在线出版日期: 2007-11-28（万方平台首次上网日期，不代表论文的发表时间）